PRODUCT DETAILS
125 DERPROOF 8: Pure Polyurea based elastomeric system. It cosists resin component 8A and isocyanate component 8B. Resin component is %100 amin based and doesn’t contain polyurethane.
125 DERPROOF 8: This dual component polyurea system based from flexible amin and aromatic isocyanate and developed for surface protection of metal, concrete, wood and EPS. It has E Class inflammable resistance according to EN 13823:2010 standard. Temperature resistance between -30C and +170C.
Apply dual component (solvent free) %100 pure epoxy lining to the clean surface with roll or similar tool approximately 250gr to square meter area. Sprinkle silica sand with 0,7-1mm thickness on wet lining to make lining surface rough.
Polyurea spray process can be started after epoxy lining dried completely. Dual component, VOC free, polyurea (A component: isocyanate and B component: polyether amin) with %500 elasticity, applied with special spray machine with 2500psi pressure at 80 Celcius temperature. After application, product drying period (gelling time) will be maximum 10 seconds and for foot traffic maximum 120 seconds will be sufficient.
Polyurea surface thicknes must be minimum 2,00 mm (2kg/m2). Critical areas like joint points should be specially treated. There shouldn’t be any pore or gap left after application completed.
Product’s tensile strength, tear resistance, hardness, elasticity, rotary abrasion, viscosity properties must be suitable with standards. Products technical properties defined in below. Product must cure quickly. Product can be applied atmospheres at low and high temperature. Product must be resistant to highly abrasive and friction effects. Product must be resistant to acids and alkali between ph3-11.
• Çok hızlı kürlenir. Jelleşme süresi: 3 saniye, Dokunma süresi: 18 saniye,
Üzerine
çıkılma süresi: 10 dakika
• Kimyasal yapısından dolayı yüksek ısılarda sıcaklık stabilitesi çok iyidir.
Isısal
olarak geniş bir uygulama aralığı vardır.-20°C dahi imalat yapılabilir.
• Membran detaylarının aksine eksiz ve yüzeyle bütünleşen bir yalıtım sistemi
oluşturur.
• Kopma uzaması % 349 (DIN 53 504)
• Gerilme Direnci 15,6 MPa (DIN 53 504)
• Düz Yırtılma Direnci 34 N/mm (DIN 53 515)
• Açılı Yırtılma Direnci 63 N/mm (DIN 53 515)
• Shore A Sertliği 96 (DIN 53 505)
• Viskozite 1000 ms (DIN 53 019) 23°C’de %50 RH
• – 45 / +150 °C arası mekanik özelliklerini muhafaza eder. Çok iyi ısı dayanımına
sahiptir.
• Basınçlı su ve bitki köklerine dayanıklıdır. Asit ve alkali dayanımı
yüksektir.
• Atmosferik koşullara karşı yüksek dayanıma sahiptir.
• Yüzey uygulama sıcaklığı:+2°C / +45°C
• E-module 3000-3200 N/mm²
• Yoğunluk(A+B Komponentleri karışımı):1,05 g/cm³
• Tam Kür Süresi(20°C,%60 R.H):1 gün